合成橡胶工业090513-橡胶技术网 www.sto.net.cn

	合成橡胶工业 CHINA SYNTHETIC RUBBER INDUSTRY 2009 Vol.32 No.5 P.404-408

团状模塑料/三元乙丙橡胶共混物的表征及其性能的影响因素

武卫莉　冯云生　

摘　要：用团状模塑料(DMC)与三元乙丙橡胶(EPDM)共混,以EPDM为连续相、DMC为分散相,制备了DMC/EPDM共混物,并对其微观结构进行了表征,研究了DMC与EPDM的质量比、过氧化物硫化荆的种类和用量以及白炭黑的用量对共混物性能的影响.结果表明,DMC和EPDM的界面作用强,相容性好;过氧化苯甲酰(BPO)作硫化荆要好于用过氧化二异丙苯;当DMC与EPDM的质量比为90/100、BPO为5份、白炭黑为50份时,共混物的力学性能和耐热老化性较好.
关键词：团状模塑料;三元乙丙橡胶;共混;力学性能;耐热老化性能
分类号：TQ333.4 　文献标识码：B
文章编号：1000-1255(2009)05-0404-05

Characterization and influencing factors on performances of dough-molding compound/ ethylene propylene diene monomer blends

Wu Weili（College of Chemistry and Chemical Engineering, Qiqihar University, Qiqihar 161006, China）　 Feng Yunsheng （College of Chemistry and Chemical Engineering, Qiqihar University, Qiqihar 161006, China）　

Abstract：Dough-molding compound (DMC)/ethylene prnpylene diene monomer (EPDM) blends were prepared, in which EPDM was used as continuous phase, and DMC as dispersed phase. The microstrueture of blends was characterized, and the influence nf DMC/EPDMI mass ratio) , species and amount of peroxide curing agents, and silica amount on the performances nf the blends were studied. The results showed that the interfaeial adhesion and compatibility between DMC and EPDM improved, the benzoperoxide(BPO) used as curing agents was better than dieumyl peroxide for the blends. The mechanical properties and heat aging resistance of the blends were better when DMC/EPDM(mass ratio) was 90/100, BPO was 5 phr, and the silica was 50 phr.
Keywords：dough-molding compound ; ethylene propylene diene monomer; blend ; mechanical property ; heat aging resistance

基金项目：Supported by Heilongjiang Science and Technology Attack Project(GC 04 A 408 -1).
作者简介：Biography:Wu Weili, doctor, professor.
作者单位：武卫莉（齐齐哈尔大学,化学与化学工程学院,黑龙江,齐齐哈尔,161006）　
　　　　　冯云生（齐齐哈尔大学,化学与化学工程学院,黑龙江,齐齐哈尔,161006）　

参考文献：

[1]Hao Yuankai,Xiao Jiayu.High Performaee Blends[M].Beijing:Chemical Industrial Press,2004:17 -19.
[2]Ye Suzhan,Zhou Yancheng,Liu Hongtao.EPDM compounding technology for heat resistance[J].World Rubber Industry,2004,31(5):10 -15.
[3]Zeng Zexin.Compounding technology of high hardness EPDM[J].World Rubber Industry,2004,31(6):12-18.
[4]Wang Yunsun.Preparation of silicon rubber/EPDM blend[J].China Rubber Industry,2005,52 (5):269.
[5]Rogers J E,Waddell W H.A review of isobutylene-based elastomers used in automotive applications[J].Rubber World,1999,224(2):24 -30.
[6]Miguel A,Lopez M C.New developments in dynamically cured PP-EPDM blends[J].Rubb Chem Technol,2001,74 (2):211 -220.
[7]Usuki A,Tukigas A,Kato M.Preparation and properties of EPDM-clay hydfid[J].Polymer,2002,43 (3):2185 -2189.
[8]Zheng Hua,Zhang Yong,Peng Zonglin,et al.EPDM/clay nanocomposite[J].合成橡胶工业,2003,26(4):226 -229.
[9]Liu Guodong,Zhang Gouwcn,Qu Xiongwei,et al.Effect of addition of EPDM grafted SAN copolymer on morphology,mechanical properties of EPDM/SAN blends[J].Polym Mater Sci Eng,2004,20(3):99 -102.
[10]Jiang Liubo.Effect factors on BMC eonstringency rate and surface gloss[J].Chem World,1998,39(2):92 -96.
[11]Wang Zhuoling.Latest rubber technology and principle[J].World Rubber Industry,2004,31 (6):47 -53.
[12]Tian Hongchi,Wu Shemao,Han Jibin,et al.Study on heat aging effect of EPDM/PP TPV[J].合成橡胶工业,2004,27 (1):34 -36.

收稿日期：2008年9月27日

出版日期：2009年9月15日

请看PDF全文