	弹性体 CHINA ELASTOMERICS 2001 Vol.11 No.1 P.21-24

N－(α－甲基－戊酯基－)马来酰亚胺树脂的合成与表征

艾娇艳　刘朋生

摘　要：以马来酸酐(MA)、D，L－氨基丙酸(Aln)、正戊醇为原料经三步二釜法合成既含不对称碳原子又含官能团(酯基)的新型马来酰亚胺单体－N－(α－甲基－戊酯基)马来酰亚胺(PAM)，并以AIBN为引发剂，用溶液聚合法合成了聚N－(α－甲基－戊酯基)马来酰亚胺，并用IR、TG、DSC对聚合物进行了表征。
关键词：N－取代马来酰亚胺；光学活性；耐热改性剂；溶液聚合
分类号：TQ326.2　文献标识码：A
文章编号：1005-3174(2001)01-0021-04

Synthesis and characterization of poly N-(α-methyl-pentyloxy carbonyl)maleimide

AI Jiao-yan（College of Chemistry and Chemical Engineering,Xiangtan University,Xiangtan　411105，China）　
LIU Peng-sheng（College of Chemistry and Chemical Engineering,Xiangtan University,Xiangtan　411105，China）　

Abstract：By using D,L-alanine,maleic anhydride and pentanol as raw materials,PAM was prepared through a new three-step and two-volume method.The poly(N-α-methyl-pentyloxy carbonyl)maleimide was successfully synthesized with benzene as solvent,2,2-Azobis(isobutyronitrile)(AIBN)as radical initiator.The resulting polymer PPAM was characterized by IR,TG and DSC,and the results were discussed.
Keywords：N-substituted maleimide;opticality;polymer heat-resistance modifier;solvent polymerization

基金项目：湖南省科委资助项目(97JKY1016-3)
作者简介：艾娇艳(1974－)，女，湖南邵阳人，在读硕士，论文方向为马来酰亚胺的不对称合成与研究。
作者单位：艾娇艳（湘潭大学化学化工学院，湖南湘潭　411105）　
　　　　　刘朋生（湘潭大学化学化工学院，湖南湘潭　411105）　

参考文献：

［1］Lnagaki Takeshi,Takayanagi Yasuyuki,Nareia Takeshi，［P］.JP，63-122，666.1988-05-26.
［2］单国荣，翁志学，黄志明，等.N－取代马来酰亚胺型高分子耐热改性剂的研究进展［J］.高分子材料，1996，(2)：36-39.
［3］单国荣，翁志学，黄志明，等.乙烯基单体－N－苯基马来酰亚胺共聚物序列结构研究［J］.高等学校化学学报，1999，20：1138.
［4］Bruno Ameduri,J.Polym.Sci.part A:Polym.Chem.，1994,32：3061-3069.
［5］Takayuki otsu et al..Polymer Bulletin［J］.1990,23:43.
［6］Tsutomu Oishi,koji Matsusaki and Mimoru Fujimoto,Polym.，1992,(24)11:1281.

收稿日期：2000年9月11日

出版日期：2001年2月1日

请看PDF全文